Schreier Metall GmbH

Cast High Lead Bronze

AlloyDensity approx.Composition
in %
Important
tempers
Tensile Strength
Rm
N/mm2
Yield Stress
Rp0,2
N/mm2
Elongation
A
%
Hardness
HB
Electr.
conductivity
MS/s
CuSn10Pb10-C
DIN EN 1982
CC495K9,0Cu 78,0 - 82,0
Sn 9,0 - 11,0
Pb 8,0 - 11,0
GC
GZ

≥ 220
≥ 220

≥ 110
≥ 110

≥ 8
≥ 6

≥ 70
≥ 70

Comparable Specifications:
CuPb10Sn, 2.1176, DIN 1716
C93700 UNS
LB 2, BS 1400


Bearing material with good sliding and dry-running properties. Good corrosion resistance and good to moderate wear resistance, suitable for high surface pressures. Very good machinability.

Product with information obligations to REACH-Legislation

CuSn7Pb15-C
DIN EN 1982
CC496K9,1Cu 74,0 - 80,0
Pb 13,0 - 17,0
Sn 6,0 - 8,0
Ni 0,5 - 2,0
GC
GZ

≥ 200
≥ 200

≥ 90
≥ 90

≥ 8
≥ 7

≥ 65
≥ 65

Comparable Specifications:
CuPb15Sn, 2.1182, DIN 1716
C93800 UNS
LB 1, BS 1400


Soft bearing material with very good sliding and dry-running properties when there is a sporadic lack of lubricant and with water lubrication. Bearings with very high surface pressures in which high edge pressure can occur. Unsuitable for temperatures above 120 °C. Resistant to sulphuric acid. Very good machinability.

Product with information obligations to REACH-Legislation

CuSn5Pb20-C
DIN EN 1982
CC497K9,3Cu 70,0 - 78,0
Pb 18,0 - 23,0
Sn 4,0 - 6,0
Ni 0,5 - 2,5
GC

≥ 180

≥ 90

≥ 7

≥ 50

Comparable Specifications:
CuPb20Sn, 2.1188, DIN 1716
C94100 UNS
LB 5, BS 1400


Very soft bearing material with excellent sliding and dry-running properties when there is a sporadic lack of lubricant and with water lubrication. But problematic with casting and rarely commercially available. For this reason usually replaced with Cu Sn7 Pb15-C.

Product with information obligations to REACH-Legislation