High Copper Alloys
DIN EN 12 163 to 12 167/12 420/12 449/1652/1654 |
|
Range of alloys |
|
approx.
Density |
Chemical
Composition % |
Comparable Specifications |
Cu Be2
|
CW101C |
8,3
|
Be 1,8 - 2,1
Cu bal. |
Cu Be2, DIN 17 666
C 17 200 UNS |
Cu Co2 Be
|
CW104C |
8,8
|
Be 0,4 - 0,7
Co 2,0- 2,8
Cu bal. |
Cu Co2 Be, DIN 17 666
C 17 500 UNS
C 112 BS 2872, 2874
A 3/1 BS 4577, ISO 5182 |
Cu Co1 Ni1 Be
|
CW103C |
8,8 |
Co 0,8 -1,3
Ni 0,8 -1,3
Be 0,4 - 0,7
Cu bal. |
C 82 200 UNS |
Cu Cr1 Zr
|
CW106C |
8,9
|
Cr 0,5 -1,2
Zr 0,03 - 0,3
Cu bal. |
Cu Cr Zr, DIN 17 666
C 18 150 UNS
CC 102 BS 2872, 2874
A 2/2 BS 4577, ISO 5182 |
Cu Ni2 Si
|
CW111C |
8,8
|
Ni 1,6 - 2,5
Si 0,4- 0,8
Cu bal. |
Cu Ni 2 Si, DIN 17 666
C 64 700, C 18 000 UNS |
| Range of alloys |
|
approx.
Density |
Chemical
Composition % |
Comparable Specifications |
*The specifications stated are similar, but might not neccessarily be identical.
|
Copper-Nickel-Alloys
DIN EN 12 163/12 420/12 449/12 451/1652/1653 |
|
Range of alloys |
|
approx.
Density |
Chemical
Composition % |
Comparable Specifications |
| Cu Ni 10 Fe 1 Mn |
CW352H |
8,9 |
Ni 9,0 -11,0
Fe 1,0 - 2,0
Mn 0,5-1,0
Cu bal. |
Cu Ni10 Fe1 Mn, DIN 17 664
C 70 600 UNS
CN 102 BS
Cu Ni10 Fe1 Mn, ISO |
| Cu Ni30 Mn1 Fe |
CW354H |
8,9 |
Ni 30,0 -32,0
Fe 0,4 -1,0
Mn 0,5-1,5
Cu bal. |
Cu Ni30 Mn1 Fe, DIN 17 664
C 71 500 UNS
CN 107 BS
Cu Ni30 Mn1 Fe, ISO |
| Range of alloys |
|
approx.
Density |
Chemical
Composition % |
Comparable Specifications |
*The specifications stated are similar, but might not neccessarily be identical.
top
|