Wrought Aluminiumbronze (Copper-Aluminium)
DIN EN 12163/12167/12420/12451/1652/1653
|
|
Range of alloys |
|
approx.
Density |
Chemical
Composition % |
Comparable Specifications* |
| Cu Al10 Fe3 Mn2 |
CW306G |
7,6
|
Al 9 -11,0
Fe 2,0 - 4,0
Mn 1,5-3,5
Cu bal. |
Cu Al10 Fe3 Mn2, DIN 17 665
C 62 300, C 62 500 UNS
CA 103 BS 2872, 2874
Cu Al10 Fe3 Mn2, ISO 428 |
| Cu Al10 Ni5 Fe 4 |
CW307G |
7,6 |
Al 8,5 -11,0
Ni 4,0 - 6,0
Fe 3,0 -5,0
Cu bal. |
Cu Al10 Ni5 Fe 4, DIN 17 665
C 63 200, C 63 000 UNS
CA 104 BS 2872, 2874, 2875
Cu Al10 Ni5 Fe 4, ISO 428 |
| Cu Al11 Fe6 Ni6 |
CW308G |
7,4
|
Al 10,5 -12,5
Ni 5,0 -7,0
Fe 5,0 -7,0
Cu bal. |
Cu Al11 Ni 6 Fe5, DIN 17 665 |
| Cu Al5 As |
CW300G |
8,2
|
Al 4,0 - 6,5
As 0,1- 0,4
Cu bal. |
Cu Al5 As, DIN 17 665
C 60 800 UNS
CA 101 BS
Cu Al5 As, ISO 428 |
| Cu Al8, DIN 17 665 |
2.0920 |
7,7 |
Al 7,0 - 9,0
Cu bal. |
C 61 000 UNS
CA 102 BS 2875
Cu Al8, ISO 428 |
| Cu Al8 Fe3 |
CW303G
|
7,7
|
Al 6,5 - 8,5
Fe 1,5 - 3,5
Cu bal. |
Cu Al8 Fe3, DIN 17 665
C 61 400 UNS
CA 106 BS 2874, 2875
Cu Al8 Fe 3, ISO 428 |
| Cu Al9 Ni3 Fe2 |
CW304G |
7,4 |
Al 8,0 - 9,5
Ni 2,0 - 4,0
Fe 1,0 -3,0
Cu bal. |
Cu Al 9 Ni3 Fe2, DIN 17 665
Cu Al 9 Ni3 Fe2, ISO 428 |
Cu Al9 Mn2,
DIN 17 665 |
2.0960 |
7,5 |
Al 8,0 -10,0
Mn 1,5 - 3,0
Cu bal. |
Cu Al9 Mn2, ISO 428 |
| Cu Al7 Si2 |
CW302G |
7,7 |
Al 6,3 - 7,6
Si 1,5 - 2,2
Cu bal. |
C 64 200 UNS |
| Range of alloys |
|
approx.
Density |
Chemical
Composition % |
Comparable Specifications |
*The specifications stated are similar, but might not neccessarily be identical.
|
Cast Aluminiumbronze (Copper-Aluminium)
DIN EN 1982 |
|
Range of alloys |
|
approx.
Density |
Chemical
Composition % |
Mechanical
Properties |
Comparable Specifications* |
| Cu Al10 Ni 3 Fe2-C |
CC332G |
7,5
|
Cu 80,0 -86,0
Al 8,5 -10,0
Ni 1,5 - 4,0
Fe 1,0 - 3,0 |
GC/GZ:
Rm > 550
Rp 0,2 > 220
A5 > 20
HB > 120 |
Cu Al 9 Ni, DIN 1714 |
| Cu Al10 Fe5 Ni5-C |
CC333G |
7,6
|
Cu 76,0- 83,0
Al 8,5 - 10,5
Ni 4,0 - 6,0
Fe 4,0 - 5,5 |
GC/GZ:
Rm > 650
Rp 0,2 > 280
A5 > 13
HB > 150 |
Cu Al10 Ni, DIN 1714
C 95 800, C 95 500 UNS
AB 2 BS 1400
Cu Al10 Fe5 Ni5, ISO 1338 |
| Cu Al11 Fe 6 Ni 6-C |
CC334G |
7,6
|
Cu 72,0 -78,0
Al 10,0 - 12,0
Ni 4,0 - 7,5
Fe 4,0 - 7,0 |
GZ/GM:
Rm > 750
Rp 0,2 > 380
A5 > 5
HB > 185 |
Cu Al11 Ni, DIN 1714 |
| Cu Al10 Fe2-C |
CC331G |
7,5
|
Cu 83,0- 89,5
Al 8,5 -10,5
Fe 1,5 - 3,5 |
GZ:
Rm > 550
Rp 0,2 > 200
A5 > 18
HB > 130 |
Cu Al10 Fe, DIN 1714
C 95 200 UNS
AB 1 BS 1400
Cu Al10 Fe3, ISO 1338 |
Cu Al8 Mn,
DIN 1714 |
2.0962 |
7,5 |
Cu min. 82,0
Al 7,0 - 9,0
Mn 5,0 - 6,5
Ni 1,0 - 2,0 |
GK:
Rm > 450
Rp 0,2 > 200
A5 > 30
HB > 105 |
|
| Range of alloys |
|
approx.
Density |
Chemical
Composition % |
Mechanical
Properties |
Comparable Specifications* |
Rm = Tensile strength in N/mm²
Rp 0,2 = Yield stress in N/mm²
A5 = Elongation in %
HB = Hardness Brinell
| We supply: |
GC
GZ
GK resp. GM
G resp. GS
|
=Continuous Cast
= Centrifugal Cast
= Chill Cast (Kokillenguss)
= Sand Cast
|
*The specifications stated are similar, but might not neccessarily be identical.